Improvement of the adhesion of conductive poly m-toluidine onto chemically reduced-wool fabrics

Authors : Meryem Kalkan Erdoğan, Meral Karakişla, Mehmet Saçak

Pages : 775-790

View : 25 | Download : 0

Publication Date : 9999-12-31

Article Type : Makaleler

Abstract :Wool has disulphide bonds containing-hydrophobic external keratin layers, which act as a barrier for the modification through coating with hydrophilic materials. For that reason, in this work, to ensure a dense and homogenous conductive polymer coating onto the wool, the fabrics were subjected to the reduction process in the aqueous alkaline medium containing agents that can attack these disulphide bonds. Then, one of the polyaniline derivatives, poly $m$-toluidine PMT , was coated onto wool by in situ polymerization of $m$-toluidine sulphate using ammonium persulfate APS as an oxidant. The effects of conditions, such as the composition of reduction-bath and types of dopants were investigated, on the mass increase % and surface resistivity of the composite. The reduction pretreatment of wool with sodium hydrosulphide significantly improved the coating density, conductivity, and colour shade of PMT on the surface, compared to an untreated one. The coating stability of PMT/wool composite was examined by rubbing test and detergent washing, through surface resistivity measurements. The changes in structural and surface properties of wool fabrics were determined with ATR-FTIR, contact angle, and optical microscopic techniques, respectively. The performance of PMT/wool composite was also examined in the electromagnetic shielding effectiveness EMSE measurements within 30 MHz-3 GHz.
Keywords : Surface modification of wool, reduction pretreatment, conductive polymer, poly $m$-toluidine, EMI shielding, rubbing stability