THE MECHANICAL CHARACTERIZATION OF CARBON BASED NANOPARTICLE REINFORCED EPOXY COMPOSITES: A COMPARATIVE STUDY

Authors : Fatih Turan

Pages : 208-221

Doi:10.18038/estubtda.1381745

View : 42 | Download : 67

Publication Date : 2024-06-28

Article Type : Research

Abstract :This comparative study experimentally investigates the effect of both the type and content of carbon based nanoparticles on the mechanical properties of epoxy composites. For this purpose, carbon nanotubes (CNTs), expanded graphite (EG), and carbon black (CB) were used as reinforcing nanoparticles at various concentrations within the epoxy polymer. The nanoparticles were dispersed by ultrasonication method. CNTs incorporated up to 0.4% by weight (wt.) while EG and CB nanoparticles were employed at 4%, 8%, 10%, and 12% concentrations by weight. Tensile tests of the nanocomposites were conducted according to ASTM D680 to determine the mechanical properties of nanocomposites including ultimate tensile strength and modulus. The results revealed that all types of nanoparticles have a strong reinforcing effect on the mechanical properties depending on their concentrations. When carbon nanotubes (CNTs) were used, the highest improvement in strength, by 84.7% at 0.1% wt., and in modulus, by 32.1% at 0.2% wt. content, was observed. EG nanoparticles exhibited improvement in both strength and modulus at all contents. The highest improvement in strength, by 109.6% at 4% wt., and in modulus, by 95.6% at 10% wt. concentration, was observed. In the case of carbon black (CB), improvement in strength was observed only at 4% wt. concentration, by 44.9%. On the other hand, enhancement in modulus was seen at all CB contents, with the greatest improvement at 10% wt., reaching 58.2%.
Keywords : Nanocomposites, Mechanical properties, Carbon nanotube, Expanded graphite, Carbon black