- Electrical Characterisation of Ni0.5Co0.3Cr0.2Mn2O4 Thermistors
Electrical Characterisation of Ni0.5Co0.3Cr0.2Mn2O4 Thermistors
Authors : Berat Yüksel Price
Pages : 401-405
Doi:10.18466/cbayarfbe.308508
View : 11 | Download : 5
Publication Date : 2017-06-30
Article Type : Research
Abstract :Negative temperature coefficient (NTC) thermistors are ceramic semiconductors derived from metal oxides such as Mn, Ni, Co, Cu, Cr, Fe etc. The electrical resistance of NTC thermistors decrease with increasing temperature. In industrial applications, the desired material constant (B) of NTC thermistors is in the range of 2000 to 5000 K and the sensitivity coefficient (α) is in the range of (-2.2) to (-5.5) %/K. The electrical properties of NTC thermistors can be changed significantly by the type and molar ratio of metal oxide additions as well as the selected process parameters during manufacturing of samples. In this study, the effect of Cr 2 O 3 addition on the electrical properties of Mn-Ni-Co-O NTC thermistors sintered at 1100 o C for 5 hours was investigated. The electrical resistance was measured in a temperature programmable furnace between 25 and 85 o C in steps of 0.1 o C. The material constant "B”, the activation energy "E a ” and the sensitivity coefficient "α” values were calculated. The aging behaviour of Mn–Ni–Co–Cr-O NTC ceramics was also investigated by electrical resistivity measurement after accelerated aging.Keywords : Aging, Chromium (III) oxide, electrical properties, NTC thermistor, sintering.