- Investigation of Sinterability of WC-Co Component Comprising of AISI 4340 Steel Inserts
Investigation of Sinterability of WC-Co Component Comprising of AISI 4340 Steel Inserts
Authors : Mehmet Subaşi, Harun Koçak, Asghar Safarian, Çetin Karataş
Pages : 1722-1731
Doi:10.35378/gujs.1070501
View : 105 | Download : 298
Publication Date : 2023-12-01
Article Type : Research
Abstract :In this study, sinterability of WC-9% Co component with AISI 4340 steel insert was investigated using Inserted Powder Injection Molding (IPIM) method. Sintering experiments were performed at temperatures of 1200 °C to 1350 °C with dwell times of 120, 240, 360 min. Defects such as gaps, cracks and macro-porosities were observed in specimens, sintered at temperatures of 1200 °C and 1250 °C for all dwell times. It was proved that sintering temperature of 1350 °C was as high as it caused insert to get deformed and melted. As a result, the optimum sintering temperature and dwell time were determined to be 1300 °C and 240 min, respectively, at which the highest hardness, compression strength, and sintered density were obtained without any defects such as cracks or gaps.Keywords : Inserted powder injection molding