- Investigation of the Production of β-Al 2 O 3 Solid Electrolyte from Seydişehir α-Al 2 O 3
Investigation of the Production of β-Al 2 O 3 Solid Electrolyte from Seydişehir α-Al 2 O 3
Authors : Zeynep Taşliçukur Öztürk, Selin Engürlü, Nilgun Kuşkonmaz
Pages : 816-819
Doi:10.19113/sdufbed.31721
View : 16 | Download : 4
Publication Date : 2017-08-08
Article Type : Other
Abstract :In this study, we report the production of β˝-Al 2 O 3 solid electrolyte by using Seydişehir α-Al 2 O 3 . Alumina has to be low grain-sized to ensure α-β phase transformation. Therefore, grain refining process was applied to high grain sized Seydişehir alumina by jetmill grinding. Seydişehir alumina was calcined at 1200 0 C for 2 hours. After calcination, calcined Al 2 O 3 and Na 2 CO 3 were mixed during 2 hours in the mill. The samples were pressed and sintered to obtain β˝-Al 2 O 3 . β˝-Al 2 O 3 was obtained after sintering at 1550°C for 1 hour. Due to the formation of β˝-Al 2 O 3 , it is observed that dielectric properties increased.Keywords : α-Al2O3, Calcination, Sintering, β-Al2O3, Dielectric properties