- Tribological behavior of epoxy nanocomposites under corrosive environment: effect of high-performanc...
Tribological behavior of epoxy nanocomposites under corrosive environment: effect of high-performance boron nitride nanoplatelet
Authors : Emine Feyza Şükür, Halil Burak Kaybal, Hasan Ulus, Ahmet Avcı
Pages : 385-395
View : 6 | Download : 24
Publication Date : 2023-04-30
Article Type : Research
Abstract :This paper sheds light on the impact of corrosive service conditions on the mechanical and tribological performances of epoxy nanocomposites containing 0.5 wt.% hexagonal boron ni-tride (BN) nanoplatelets as fillers. The composite samples were aged in 10 wt% H2SO4 solu-tions by immersion for 504 hours. Variation in mechanical and tribological behaviors during immersion was investigated using tensile and ball-on disk tests. The ball-on disk tests were performed at room temperature under a 10 N constant load and 0.8 m/s speed for 3000 sec-onds. The high-performance BN nanoplatelets improved neat Epoxy’s tensile strength, tough-ness, and wear performance by 17%, 27%, and 56%, respectively. The aging results revealed that H2SO4 exposure deteriorates the mechanical performance of all epoxy composite samples, even though BN/Epoxy nanocomposites exhibited better resistance to the corrosive environ-ment. In contrast, the tribological performance increased with the acidic solution exposure that acts as a lubricant and forms a corrosive protective layer after the immersion of 504 hoursKeywords : Corrosive Environment, Ball-On Disk, Epoxy, Hexagonal Boron Nitride, Sulphuric Acid, Wear